VEKAPLAN S are foam sheets made of rigid PVC with excellent properties. They are produced by the Celuka process. The uniform inner cell structure as well as the smooth homogeneous surface on both sides is achieved by the help of this process.
| Properties | Norm | VEKAPLAN S | ||
| Thickness [mm] | 8, 10, 13, 15, 17 | 19, 24 | 30 | |
| Density [g/cm³] | DIN EN ISO 1183 | 0,42 - 0,55 | 0,42 - 0,55 | 0,42 - 0,55 |
| E-modulus [Mpa] | ISO 527 (50 mm/min) | * 1050 | * 1050 | * 1050 |
| Notched impact resistance (Charpy) [kj/m²] | ISO 179/1eA | *20 | *20 | *20 |
| Tensile strength [Mpa] | ISO 527 (50 mm/min) | *11 | *11 | *11 |
| Flexural strength [Mpa] | ISO 178 (2 mm/min) | *21 | *21 | *21 |
| Shore-hardness D | ISO 868 | 66 - 70 | - | - |
| Surface resistance ROE [Ω] | DIN IEC 60 167 | 2,00E+14 | - | - |
| Volume resistance RD [Ω] | DIN IEC 60 093 | 1,86E+14 | - | - |
| Dielectric constant εr | DIN 53 483 | 1,6 - 1,8 | - | - |
| Coefficient of expansion (104/K) | DIN 53 752 | 6 · 10-5 | 6 · 10-5 | 6 · 10-5 |
| Compressive strength [N/mm²] | DIN 53 421 | 3,5 | - | - |
| Vicat softening point [°C] | ISO 306 (B 50) | 49 | 49 | 49 |
| Heat distortion temperature [°C] | ISO 75-2 (1,8 Mpa) | 57 | 57 | 57 |
| Water absorption [%] | ISO 62 (after 216 h) | 4,9 | 4,9 | 4,9 |
| Water vapour - diffusion equivalent Sd [m] | DIN 52 615 | 157 (for 10 mm) | - | - |
| Fire Behaviour | DIN 4102 | B2 | B1 | B2 |
| Properties | Norm | VEKAPLAN S | ||||||
| Thickness [mm] |  | 8 | 10 | 13 | 17 | 19 | 24 | 30 |
| Thermal conductivity [W/mK] | DIN 52 612 | 0,049 | 0,051 | 0,053 | 0,057 | 0,060 | 0,062 | 0,067 |
| U-Value [W/m2K] | DIN 52 612 | 3,0 | 2,8 | 2,4 | 2,2 | 2,0 | 1,8 | 1,6 |
| Sound insulation value [dB] | DIN ISO 717-1 | 26 | 27 | 28 | 30 | 30 | 31 | 32 |
Length | Width | Thickness |
+10,0 mm | +6,0 mm | ±(0,08 mm + 0,03mm x S) |
-0,0 mm | -0,0 mm | |